品名:銅基非晶體焊片
品牌:HUAZHONG華眾
牌號:HZCu-7
熔點:560－640攝氏度
厚度:0.03-0.06
寬度:4mm以上
適用方法:電阻焊
本產(chǎn)品屬于環(huán)保焊料,外觀為,青銅顏色的箔帶,流動性好,焊縫美觀,焊接強度高,可以代替銀焊片，廣泛應用于精密儀表,電路和元器件、觸頭、熱交換器等的焊接, 銀觸點的焊接,以及銅及銅合金的釬焊,接點強度可達98－137MPa.
博威包裝規(guī)格:盤裝,每盤2-3公斤左右.

HUAZHONG Broadway Cu amorphous Soldering (BWCu-7): melting point 560 ℃ -640 ℃, brazing temperature of 700 ℃ -750 ℃, can replace the piece of silver solder is widely used in precision instruments, circuits and components, contact , heat exchanger welding, as well as copper and copper alloy brazing, joints strength up to 98-137MPa. Broadway Packing: Thickness (0.03mm-0.05mm), width of any width from 5mm to 100mm. and provides sample trial.

*HUAZHONG華眾鎳基非晶焊片(BWNi-7):熔點960℃－990℃,釬焊溫度1040℃－1100℃,主要應用于釬焊耐熱鋼,高溫合金及不銹鋼零部件。釬料高溫強度高,潤濕性極好.釬縫在500度左右可以長期工作,廣泛用于燃油總管,導管,噴嘴,整流器,擴壓器等零部件的焊接.接點強度137－156MPa.
華眾包裝規(guī)格:厚度(0.03mm-0.05mm),寬度從5mm至100mm任意寬度.并可提供樣品試用.

* HUAZHONG Broadway welding nickel-based amorphous films (BWNi-7): melting point 960 ℃ -990 ℃, brazing temperature 1040 ℃ -1100 ℃, brazing is mainly used in heat-resistant steel, high temperature alloy and stainless steel parts and Pieces. Solder temperature, high strength, excellent wettability. Brazing seam at 500 degrees can be long-term work, widely used in fuel mains, ducts, nozzles, rectifier, diffuser, and other parts of the welding joints strength 137-156MPa. Broadway Package Specifications: Thickness (0.03mm-0.05mm), width of any width from 5mm to 100mm. trial could provide samples.